Pengaruh Viskositas Terhadap Kehomogenan Dan Ketebalan Lapisan Rgo Pada Karakterisasi Surface Plasmon Resonance

Syarifuddin, Imam Mahdi and Dr. Eng. Masruroh, S.Si., M.Si. and Ir. D. J. Djoko H. Santjojo, M.Phil., Ph.D. (2024) Pengaruh Viskositas Terhadap Kehomogenan Dan Ketebalan Lapisan Rgo Pada Karakterisasi Surface Plasmon Resonance. Sarjana thesis, Universitas Brawijaya.

Abstract

Lapisan rGO yang dideposisikan diatas fiber optik dapat mempengaruhi efektivitas kinerja Surface Plasmon Resonance (SPR). Pada penelitian ini bertujuan untuk menganalisis pengaruh viskositas terhadap ketebalan lapisan rGO yang dideposisikan di atas fiber optik. Viskositas rGO salah satunya dipengaruhi oleh konsentrasi massa pereduksi dimana dalam penelitian ini digunakan Asam Askorbat (AA). Viskositas larutan diukur dengan Viskometer Brookfield menunjukkan penambahan konsentrasi menambah kekentalan larutan, sehingga semakin besar konsentrasi massa asam askorbat maka viskositas larutannya semakin tinggi. Dengan metode spin coating, rGO dideposisi di atas fiber optik dan memberikan data ketebalan yang sesuai dengan tingkat viskositas larutan, yaitu A1=618,83 mPA.s; A2=640,17 mPA.s; A3 924,5 mPA.s. Dengan variasi asam askorbat mempengaruhi gugus fungsi, dimana juga mempengaruhi ketebalan lapisan sehingga didapatkan ketebalan lapisan yaitu 618,83 nm; 640,17 nm; dan 924,5 nm. Hanya sampel A1 dan A2 yang dapat di uji SPR karena diketahui bahwa kedalaman penetrasi pada gelombang evanescent tidak boleh lebih dari panjang gelombang yang digunakan, sedangkan pada A3 ketebalan lapisan melebihi panjang gelombang tersebut. Dalam pengujian SPR didapatkan kesimpulan bahwa penambahan rGO dengan perbedaan kehomogenan dan ketebalan mempengaruhi transmitansi dan FWHM pada karakteristik SPR, dimana semakin homogen dan tebal mengakibatkan penurunan transmitansi, selain itu juga terjadi peningkatan FWHM pada A1 dan A2. Hal ini dikarenakan terjadinya peningkatan penyerapan hamburan cahaya pada fiber optik.

English Abstract

The rGO layer deposited on top of optical fiber can affect the effectiveness of Surface Plasmon Resonance (SPR) performance. This study aims to analyze the effect of viscosity on the thickness of the rGO layer deposited on top of the optical fiber. The viscosity of rGO is influenced by the concentration of reducing mass where in this study Ascorbic Acid (AA) is used. The viscosity of the solution measured with a Brookfield Viscometer shows that the addition of concentration increases the viscosity of the solution, so that the greater the mass concentration of ascorbic acid, the higher the viscosity of the solution. With the spin coating method, rGO was deposited on top of the optical fiber and gave thickness data corresponding to the viscosity level of the solution, namely A1 = 618.83 mPa.s; A2 = 640.17 mPa.s; A3 924.5 mPa.s. With the variation of ascorbic acid affecting the functional groups, which also affects the thickness of the coating so that the thickness of the coating is obtained, namely 618.83 nm; 640.17 nm; and 924.5 nm. Only samples A1 and A2 can be tested for SPR because it is known that the penetration depth of evanescent waves cannot be more than the wavelength used, while in A3 the layer thickness exceeds the wavelength. In the SPR test, it was concluded that the addition of rGO with different homogeneity and thickness affects the transmittance and FWHM in SPR characteristics, where the more homogeneous and thicker results in a decrease in transmittance, besides that there is also an increase in FWHM in A1 and A2. This is due to an increase in the absorption of light scattering on the optical fiber.

Text (DALAM MASA EMBARGO) IMAM MAHDI SYARIFUDDIN.pdf Restricted to Registered users only Download (3MB)

Actions (login required)

View Item